Implementeringsstandarder: GB/T8162 sömlöst stålrör för struktur, GB/T8163 sömlöst stålrör för vätsketransport. 0420D och 0420E mekaniska egenskaper: draghållfasthet 520~680MPa,<16 service strength 2420MPa, 16mm~30mm service strength 2400, 230mm Yield strength 2380MPa Impact test Q420D minus 20C Impact energy 234, impact test Q420E minus 40C Impact energy 227 :0.20, chromium: <0.30, nickel: <0.50, copper: 0.20, nitrogen: 0.015, :0.20, aluminum, 20.015.Q420E seamless steel pipe chemical composition: carbon: 0.20, silicon: 0.50, :1.70, phosphorus: 0.025, Sulfur: 0.020, : 0.07, : 0.20, : 0.20 Chromium: <0.30, Nickel: <0.50, Copper: <0.20, Nitrogen: 0.015, : 0.20, Aluminum, 20.015. Steel refining method: Steel should be processed by electric arc furnace Refining outside the furnace or gas converter plus outside refining method. After negotiation between the supply and demand parties, other methods with higher requirements can also be used to treat refining. When the demander requires a certain refining method, it should be stated in the contract.
Rörtillverkningsmetod: Rör kan också tillverkas genom kontinuerlig gjutning, formgjutning eller varmvalsning.
Stränggjutna rör bör också uppfylla bestämmelserna i YB/T 4149; varma rör bör också uppfylla bestämmelserna i YB/T 5221 eller YB/T 5222; formgjutna rör kan också hänvisa till bestämmelserna om varma (smidda) rör.