Kvalitet av rostfritt stålrör

Material	ASTM-betyg	UNS-betyg	DIN-klass	JIS-betyg	Namn på stål
Austenitisk	TP 304	S30400	1.4301	SUS304TB	X5CrNi18-20
	TP 304L	S30403	1.4306		X2CrNi19-11
	TP 304L	S30403	1.4307	SUS304LTB	X2CrNi18-9
	TP 304H	S30409	1.4948	SUS304HTB	X6CrNi18-10
	TP 310S	S31008	1.4845	SUS310STB	X8CrNi25-21
	TP 310H	S31009
			1.4335		X1CrNi25-21
	TP 316	S31600	1.4401	SUS316TB	X5CrNiMo17-12-2
	TP 316L	S31603	1.4404	SUS316LTB	X2CrNiMo17-12-2
	TP 316H	S31609	1.4918	SUS316HTB	X6CrNiMo17-13-2
	TP 316Ti	S31635	1.4571	SUS316TiTB	X6CrNiMo17-12-2
	TP 321	S32100	1.4541	SUS321TB	X6CrNiNb18-10
	TP 312H	S32109	1.4941	SUS321HTB	X6CrNiTiB18-10
	TP 347	S34700	1.455	SUS347TB	X6CrNiNb18-10
	TP 347H	S34709	1.4912	SUS347HTB	X7CrNiNb18-10
Ferritisk & Martensitisk	TP 405	S41500	1.4002	SUS 405TB	X6CrAl13
	TP 410	S41000	1.4006	SUS 410TB	X12Cr13
	TP 430	S43000	1.4016	SUS 430TB	X6Cr17
Ferritisk / Austenitisk		UNS S31803
	2205	UNS S32205	1.4462		X2CrNiMoN22-5-3
	2507	UNS S32750	1.441		X2CrNiMoN25-7-4
		UNS S32760	1.4501		X2CrNiMoCuWN25-7-4

Standard för rostfritt stålrör

A 213 / SA 213	Sömlösa ferritiska och austenitiska legerade stålpanna, överhettare och värmeväxlarrör
A 249 / SA 249	Svetsad austenitisk stålpanna, överhettare, hörväxlare och kondensorrör
A 268 / SA 268	Sömlösa och svetsade ferritiska och martensitiska rostfria rör för allmän service
A 269	Sömlösa och svetsade austenitiska rostfria stålrör för allmän service
A 312 / SA 312	Sömlösa, svetsade och kraftigt kallbearbetade austenitiska rör i rostfritt stål
A 376 / SA 376	Sömlöst austenitiskt stålrör för högtemperaturservice
A 688 / SA 688	Sömlösa och svetsade austenitiska matarvattenvärmarrör i rostfritt stål
A 789 / SA 789	Sömlösa och svetsade ferritiska/austenitiska rör av rostfritt stål för allmän service
A 790 / SA 790	Sömlöst och svetsat ferritiskt/austenitiskt rostfritt stålrör
A 999 / SA 999	Allmänna krav för rör av legerat och rostfritt stål
A 1016 / SA 1016	Allmänna krav för ferritiskt legerat stål, austenitiskt legerat stål och rostfria stålrör
Europeisk standard
DIN EN 10216-5	Sömlösa stålrör för tryckändamål
DIN EN 10217-7	Svetsade stålrör för tryckändamål
DIN EN 10297-2	Sömlösa stålrör för mekaniska och allmänna tekniska ändamål
DIN EN 10305-1	Stålrör för precisionsapplikationer
tysk standard
DIN 11850	Rostfria stålrör för livsmedels- och kemiska industrier-mått, material
DIN 17455	Allmänt svetsade cirkulära rör av rostfritt stål
DIN 17456	Allmänna sömlösa cirkulära rör i rostfritt stål
DIN 17457	Svetsade cirkulära austenitiska rör av rostfritt stål omfattas av särskilda krav
DIN 17458	Sömlösa cirkulära austenitiska rör av rostfritt stål omfattas av särskilda krav
DIN 28180	Sömlösa stålrör för värmeväxlare
DIN 11850	Svetsade rör och rör för livsmedels-, dryckes-, kemi- och läkemedelsindustrin
Rysk standard
GOST 9941	Sömlösa och varmdeformerade rör tillverkade av korrosionsbeständigt stål
Norsok Standard
Norskok M - 650	Kvalificering av tillverkare av specialmaterial
Norskok M - 630	Materialdatablad och elementdatablad för rörledningar

Kemiska krav (%)

Kvalitet	UNS Design	C	Mn	P	S	Si	Hp	Ni	MB	Ti	Obs	Ta	N	Vn	Cu	Ce	B	Al	Övrig
TP304	S30400	0.08	2	0.045	0.03	1	18.0–20	8.0–11	. . .	. . .	. . .	. . .	. . .	. . .	. . .	. . .
TP304L	S30403	0.035	2	0.045	0.03	1	18.0–20	8.0–13	. . .	. . .	. . .	. . .	. . .	. . .	. . .	. . .
TP304H	S30409	0.04 – 0.1	2	0.045	0.03	1	18.0–20	8.0–11	. . .	. . .	. . .	. . .	. . .	. . .	. . .	. . .
TP310S	S31008	0.08	2	0.045	0.03	1	24.0- 26	19.0- 22	0.75	. . .	. . .	. . .	. . .	. . .	. . .	. . .
TP310H	S31009	0.04 - 0.1	2	0.045	0.03	1	24.0–26	19.0–22	. . .	. . .	. . .	. . .	. . .	. . .		. . .
TP310H	S31035	0.04 - 0.1	0.6	0.025	0.015	0.4	21.5–23.5	23.5–26.5	. . .	. . .	0.40- 0.6	. . .	0.20- 0.3	. . .	2.5- 3.5	. . .	0.002- 0.008		Se Spec
TP316	S31600	0.08	2	0.045	0.03	1	16.0–18	10.0–14	2.00–3	. . .	. . .	. . .	. . .	. . .	. . .	. . .
TP316L	S31603	0.035	2	0.045	0.03	1	16.0–18	10.0–14	2.00–3	. . .	. . .	. . .	. . .	. . .	. . .	. . .
TP316H	S31609	0.04 – 0.1	2	0.045	0.03	1	16.0–18	10.0–14	2.00–3	. . .	. . .	. . .	. . .	. . .	. . .	. . .
TP317	S31700	0.08	2	0.045	0.03	1	18.0–20	11.0–15	3.0–4	. . .	. . .	. . .	. . .	. . .	. . .	. . .
TP317L	S31703	0.035	2	0.045	0.03	1	18.0–20	11.0–15	3.0–4	. . .	. . .	. . .	. . .	. . .	. . .	. . .
TP321	S32100	0.08	2	0.045	0.03	1	17.0–19	9.0–12	. . .	Ti 5 × (C+N) min, 0,70 max	. . .	. . .	0.1	. . .	. . .	. . .
TP321H	S32109	0.04 – 0.1	2	0.045	0.03	1	17.0–19	9.0–12	. . .	4(C+N) min; 0.70 max	. . .	. . .	0.1	. . .	. . .	. . .
TP321H	S32654	0.02	2.0-4	0.03	0.005	0.5	24.0–25	21.0–23	7.0-8	. . .	. . .	. . .	0.45- 0.55	. . .	0.30-0.6	. . .
TP321H	S33228	0.04 - 0.08	1	0.02	0.015	0.3	26.0–28	31.0–33	. . .	. . .	0.60- 1	. . .	. . .	. . .	. . .	0.05 - 0.1		0.025
TP321H	S34565	0.03	5.0-7	0.03	0.01	1	23.0–25	16.0–18	4.0-5	. . .	0.1	. . .	0.40- 0.6	. . .	. . .	. . .
TP347	S34700	0.08	2	0.045	0.03	1	17.0–19	9.0–13	. . .	. . .	Se Spec	. . .	. . .	. . .	. . .	. . .
TP347H	S34709	0.04 – 0.1	2	0.045	0.03	1	17.0–19	9.0–13	. . .	. . .	Se Spec	. . .	. . .	. . .	. . .	. . .
Legering 20	N08020	0.07	2	0.045	0.035	1	19.0–21	32.0–38	2.0–3	. . .	Se Spec	Se Spec	. . .	. . .	3.0– 4	. . .	. . .	. . .
Legering 20	N08367	0.03	2	0.04	0.03	1	20.0–22	23.5–25.5	6.0–7	. . .	. . .	. . .	0.18–0.25	. . .	0.75	. . .	. . .	. . .
Legering 20	N08028	0.03	2.5	0.03	0.03	1	26.0–28	30.0–34	3.0–4						0.60–1.4
Legering 20	N08029	0.02	2	0.025	0.015	0.6	26.0–28	30.0–34	4.0–5						0.6– 1.4

Värmebehandlingsdiagram

Kvalitet	UNS Beteckning	Avsluta	Uppvärmningstemperatur
TP304H	S30409, S30415	Kall	1900 grader F [1040 grader ]
TP304H	S30409, S30415	Varm	1900 grader F [1040 grader ]
TP310H	S31009		1900 grader F [1040 grader ]
TP310H	S31035		2160-2280 grad F [1180-1250 grad ]
TP316H	S31609	Kall	1900 grader F [1040 grader ]
TP316H	S31610	Varm	1900 grader F [1040 grader ]
TP321H	S32109, S32615	Kall	2000 grader F [1100 grader ]
TP321H	S32109, S32615	Varm	1925 grader F [1050 grader ]
TP321H	S32654		2100 grader F [1150 grader ]
TP321H	S33228		2050-2160 grad F [1120-1180 grad ]
TP321H	S34565		2050-2140 grad F [1120-1170 grad ]
TP347H	S34709	Kall	2000 grader F [1100 grader ]
TP347H	S34709	Varm	1925 grader F [1050 grader ]
Legering 20	N08020		1700-1850 grad F [925-1010 grad ]
Legering 20	N08367		2025 grader F [1110 grader ]
Legering 20	N08028		2000 grader F [1100 grader ]
Legering 20	N08029		2000 grader F [1100 grader ]

Draghållningskrav

Kvalitet	UNS-beteckning	Draghållfasthet, min ksi [MPa]	Avkastning Styrka, min ksi [MPa]	Övrig
TP304	S30400	75 [515]	30 [205]
TP304L	S30403	70 [485]	25 [170]
TP304H	S30409	75 [515]	30 [205]
TP304H	S30415	87 [600]	42 [290]
TP310S	S31008	75 [515]	30 [205]
TP310H	S31009	75 [515]	30 [205]
TP310H	S31035	95 [655]	45 [310]
TP316	S31600	75 [515]	30 [205]
TP316L	S31603	70 [485]	25 [170]
TP316H	S31609	75 [515]	30 [205]
TP316H	S31635	75 [515]	30 [205]
TP317	S31700	75 [515]	30 [205]
TP317L	S31703	75 [515]	30 [205]
TP317L	S31725	75 [515]	30 [205]
TP317L	S31726	80 [550]	35 [240]
TP317L	S31727	80 [550]	36 [245]
TP317L	S31730	70 [480]	25 [175]
TP317L	S32053	93 [640]	43 [295]
TP321	S32100	75 [515]	30 [205]	svetsad och sömlös
TP321	S32100	75 [515]	30 [205]	t=0.375 tum.
TP321	S32100	70 [480]	25 [170]	t > 0.375 tum.
TP321H	S32109	75 [515]	30 [205]	svetsad och sömlös
TP321H	S32109	75 [515]	30 [205]	t=0.375 tum.
TP321H	S32109	70 [480]	25 [170]	t > 0.375 tum.
TP321H	S32615	80 [550]	32 [320]
TP321H	S32654	109 [750]	62 [430]
TP321H	S33228	73 [500]	27 [185]
TP321H	S34565	115 [795]	60 [415]
TP347	S34700	75 [515]	30 [205]
TP347H	S34709	75 [515]	30 [205]
Legering 20	N08020	80 [550]	35 [240]
Legering 20	N08028	73 [500]	31 [214]
Legering 20	N08029	73 [500]	31 [214]
Legering 20	N08367	100 [690]	45 [310]	t=0.187 tum.
Legering 20	N08367	95 [655]	45 [310]	t > 0.187 tum.